A-P24C
A-P24C low-halogen flame-retardant granule for styrenics and PC/ABS
A-P24C is documented as uniform bright white granule for ABS / PC/ABS / HIPS / GPPS / XPS / EPS. The source TDS lists ABS 25%; HIPS/XPS/EPS/GPPS 15%; PC/ABS 15% and positions the grade for resin-specific flame-retardant formulation trials.
25 kg plastic compound bag
TDS-derived technical profile
Key values listed for A-P24C
The following technical values are taken from the current TDS to support grade selection and initial formulation work.
| Property | Listed value | Condition |
|---|---|---|
| Listed dosage | ABS 25%; HIPS/XPS/EPS/GPPS 15%; PC/ABS 15% | — |
| TDS flame classification | UL94 V-0 direction | — |
| Effective flame-retardant content | 85-90% | — |
| Oxygen index | 35 | Source comparison table |
| Sample thickness | 1.6 mm | Source comparison table |
| Halogen statement | Low-halogen | Source TDS wording |
What this grade is positioned to support
- Flame-retardant formulation evaluation
- Direct-add processing trial
- Thickness-specific verification
How to prepare the first evaluation
- 01
Pre-dry A-P24C for 2 hours at 80-90°C.
- 02
Blend directly with the listed resin without an added synergist during the first trial.
- 03
Verify flame class on the final formulation and thickness.
Technical documentation
Request current TDS Current TDS and application guidance
Source file: a-p24c-tds.pdf. UL94 and oxygen-index statements require current evidence on the final formulation and thickness. Fillers, pigments, resin grade and processing temperature can materially change flame performance.